Info product

Info product (14)

May 2023

 

 

 

ZYTTRIA® Z MULTICOLOR ANTERIOR   900-600Mpa

 

3D progressive multilayer isostatic zirconia
The predominantly cubic crystalline structure ensures a high degree of translucency and extraordinary resistance to aging properties.
 

 

Gradual colour, translucency and mechanical resistance from the incisal area
to the cervical area for a very natural effect,
aesthetics comparable to Lithium Disilicate.
 
Very high progressive translucency
Thanks to its exceptional translucency, it is a valid alternative to lithium disilicate.
 
High aging resistance

High strength thanks to the crystalline structure characterized by 50% cubic phase.

 
Progressive mechanical resistance

From 900 mpa (marginal part) to 600 mpa (incisal part), exceptional for the anterior area,

but also suitable for small posterior bridges.

 
Applications     Single crowns, veneers, inlays, onlays, 3/5 element bridges.
 
                          The high resistance value at the base allows to realize
                           bridges up to 5 elements (1 missing) in the front area.
 
Colors               • A1 (A1.8-A0.5)* • A2 (A2.5-A1)* • A3 (A3.5 - A1.5)* • A3.5 (A4 - A2)*
                                • C2 (C3 - C1)* • D2 (D4 - D2)*                              *Indicative values, approximated to the Vita® scale
 
                                Enamel area thickness > 3mm.
 

Characterization  In the green phase infiltration with colors AQUA-P ANTERIOR
 
 
 
 

Progression of chromatic intensity, mechanical resistance and translucency in the six layers

 
 
 


 

 

 
 
 
 

 

Nov 2018
30 January 2017

Products

Written by

ZYTTRIA®
Z MULTICOLOR ANTERIOR

Multilayer Zirconia. Cubic structure in 6 layers. Gradual ultra translucency, gradual resistance from 600 to 900 Mpa.

 

 

More info

ZYTTRIA®
Z MULTICOLOR SUPER-TRASLUCENT

Multilayer Zirconia. Naturally gradual super translucency. Resistance 1000 Mpa (only enamel layer 600 Mpa).

 

 

More info

ZYTTRIA®
Z MULTICOLOR EXTRA-PLUS

Multilayer Zirconia. High mechanical resistance, gradual from 1200 to 900Mpa. Particularly stable, perfect for complex geometries.

 

More info

ZYTTRIA®
Z COLOR ANTERIOR 

Multilayer Zirconia. High mechanical resistance, gradual from 1200 to 900Mpa. Particularly stable, perfect for complex geometries .

More info

ZYTTRIA®
Z COLOR SUPER-TRASLUCENT

Super translucent Zirconia with high mechanical values to manufacture from crowns to long bridge.

 

More info

ZYTTRIA®
Z COLOR EXTRA-PLUS

Precoloured monolayer translucent Zirconia with high mechanical values for any prosthetic restoration, complex as well.

 

More info

Z ZYTTRIA®
Z403 ANTERIOR

Pure white Zirconia. Ultra translucency >49%. Resistance 600 Mpa. Esthetic results comparable to Lithium Disilicate.

 

 

More info

ZYTTRIA®
Z404 SUPER-TRASLUCENT

Pure white Zirconia. Super translucency >45%. High resistance = 1000 Mpa to manufacture esthetic and functional restorations, extended as well.

 

More info

ZYTTRIA®
Z402 EXTRA-TRASLUCENT PLUS

Pure white Zirconia. High translucency >41% and high resistance > 1100 Mpa. Esthetic and high functional performances, for monolithic full denture as well.

More info

ZYTTRIA® Z401 WHITE TRASLUCENT

Pure white Zirconia. High mechanical resistance >1200Mpa for restorations to be layered with ceramic.

More info

ZYTTRIA® Z402 EXTRA-TRASLUCENT

Pure white Zirconia. High translucency for crowns and monolithic bridges.

 

More info

PROCESSING in LAB

Accessories for sintering, ceramic layering, detecting.

 

More info

AQUA – Water based colour liquids

Liquids for colouring Zirconia in green state, with infiltration by dipping or by brushing.

 

More info

RESIN & WAX

Milling resin materias, PMMA and waxes for provisionals and for modeling.

 

More info

MILLING BURS

Milling burs for Zirconia. Top quality with diamond coating. Superior cutting and lifespan performances.

More info
 
30 January 2017

Zirconia

Written by

Raw Material

Zirconium oxide, ceramic material not to be confused with Zirconium, metal

More Info

Medical Zirconia

Biocompatibility and aesthetic for high quality dental restoration

More Info

Not all Zirconia is the same

Discs look similar from outside, they are very different "inside"

More Info

Japanese powders

Only Japanese raw material for high quality Zirconia

More Info

Axial or isostatic pressing?

Are there differences between two technologies? More quality with isostatic "single cip" pressing by Concept

More Info

Pre-sintering

Delicate process, fundamental for machinability in the laboratory

More Info

Quality control

Quality control on every stage of production

More Info

Biocompatibility

100% bio-compatible The importance to be metal-free.

More Info

Radioactivity

Zirconia Zyttria® has radioactivity values much lower than human saliva

More Info
 
 
 
14 December 2016

Compatible cad cam system Wieland*

Written by

 

ZYTTRIA® Z401 WHITE TRASLUCENT

APPLICATIONS

Zirconia Zyttria ® Z401 WHITE TRASLUCENT is suitable for realizing crowns, bridges and arches to be layered with ceramic.

 

DESCRIPTION

Isostatic Zirconium Oxide with high mechanical resistance and high resistance to aging..

Thanks to “single cip” isostatic pressing technology is incredibly stable, granting a perfect dimensional precision even in larger structures.

Sintering temperature: 1450°C

 

COLOURING

Colour liquids for dipping technique AQUA-W.

 

Item Code Description Pieces/Pack
C98000WO1 DISC   WØ98   H10mm 1
C98001WO1 DISC   WØ98   H12mm 1
C98002WO1 DISC   WØ98   H14mm 1
C98003WO1 DISC   WØ98   H16mm 1
C98004WO1 DISC   WØ98   H18mm 1
C98005WO1 DISC   WØ98   H20mm 1
C98007WO1 DISC   WØ98   H25mm 1

ZYTTRIA® Z402 EXTRA-TRASLUCENT PLUS

APPLICATIONS

Zirconia Zyttria ® Z402 EXTRA-TRASLUCENT PLUS is suitable for realizing individual crowns, bridges and circulars layered with ceramic or completely anatomic .

 

DESCRIPTION

New generation isostatic Zircomium Oxide with high translucency to meet the needs of dental technicians .

High mechanical performances in terms of flexural resistance to fracture are combined with great aesthetic properties to achieve a "true to nature" result.

Sintering temperature:  1450°C/1500°C/1550°C

 

COLOURING

Colour liquids for dipping technique AQUA-T Plus.

Colour liquids for brushing technique AQUA-P.

 

Item Code Description Pieces/Pack
C98000WT1-Plus DISC   WØ98   H10mm 1
C98001WT1-Plus DISC   WØ98   H12mm 1
C98002WT1-Plus DISC   WØ98   H14mm 1
C98003WT1-Plus DISC   WØ98   H16mm 1
C98004WT1-Plus DISC   WØ98   H18mm 1
C98005WT1-Plus DISC   WØ98   H20mm 1
C98007WT1-Plus DISC   WØ98   H25mm 1 

ZYTTRIA® Z403 ANTERIOR

APPLICATIONS

Zyttria ® Z403 ANTERIOR is suitable especially for anterior teeth, for realizing individual crowns, inlays, onlays, veneers and bridges with maximum 3 elements.

 

DESCRIPTION

Zirconium Oxide with high translucency, comparable to Lithium Disilicate but with a double resistance (600 Mpa).

Dry or water milling.

Sintering temperature:  1450°C

 

COLOURING

Colour liquid for brushing technique AQUA-P for Anterior.

 

 

Item Code Description Pieces/Pack
C98001WA3 DISC   WØ98   H12mm 1
C98002WA3 DISC   WØ98   H14mm 1
C98004WA3 DISC   WØ98   H18mm 1
C98005WA3 DISC   WØ98   H20mm 1
C98007WA3 DISC   WØ98   H25mm 1

Z COLOR ANTERIOR

APPLICATIONS

  • Individual crowns
  • Inlays, onlays, veneers
  • Bridges with max. 3 elements

All restorations can be realised in fully anatomic version or layered with ceramic.

 

DESCRIPTION

Zyttria ® Z COLOR ANTERIOR, high precoloured translucent  Zirconia with resistance to flexion of 600 MPa, is suitable for realising dental restorations in which a extremely refined aesthetic is required, that is the anterior area.

Grazie Thanks to its reesistance and stability  is suitable for posterior or lateral areas as well where is possible to realise bridges with max. 3 elements.

 

PROCESSING

Dry or water milling with milling machines suitable forZirconia.

Sintering temperature: 1450°C

 

COLOURING

Colour liquid for brushing technique AQUA-P for Anterior.

  

Item Code Description Pieces/Pack
C98002WZ3C05AANT DISC   WØ98   H14mm - A1 1
C98002WZ3C08AANT DISC   WØ98   H14mm - A2 1
C98002WZ3C10AANT DISC   WØ98   H14mm - A3 1
C98002WZ3C08BANT DISC   WØ98   H14mm - B2 1
C98004WZ3C05AANT DISC   WØ98   H18mm - A1 1
C98004WZ3C08AANT DISC   WØ98   H18mm - A2 1
C98004WZ3C10AANT DISC   WØ98   H18mm - A3 1
C98004WZ3C08BANT DISC   WØ98   H18mm - B2 1

 

 

ZYTTRIA® Z COLOR EXTRA-PLUS

APPLICATIONS

Zyttria ® Z COLOR EXTRA-PLUS is suitable for realizing individual crowns, bridges and fully anatomic circulars.

 

DESCRIPTION

Precoloured isostatic Zirconium Oxide with high translucency and high mechanical resistance.

The colouring of the prosthetic device, after sintering, results uniform and homogeneous on the whole piece.

Available in four shades Light / Medium / Intensive / Grey  Light, the ideal base to reproduce the natural colour of the patient.

Sintering temperature:  1450°C/1500°C/1550°C

 

COLOURING

Colour liquids for brushing technique AQUA-P.


 

 

 

Item Code Description Colour Pieces/Pack

Z COLOR  05 - LIGHT

C98002WZ1C05A-Plus DISC   WØ98   H14mm    LIGHT 1
C98003WZ1C05A-Plus DISC   WØ98   H16mm LIGHT 1
C98004WZ1C05A-Plus DISC   WØ98   H18mm LIGHT 1
C98005WZ1C05A-Plus DISC   WØ98   H20mm LIGHT 1
C98007WZ1C05A-Plus DISC   WØ98   H25mm LIGHT 1

Z COLOR  20 - MEDIUM

     
C98002WZ1C20A-Plus DISC   WØ98   H14mm MEDIUM 1
C98003WZ1C20A-Plus DISC   WØ98   H16mm MEDIUM 1
C98004WZ1C20A-Plus DISC   WØ98   H18mm MEDIUM 1
C98005WZ1C20A-Plus DISC   WØ98   H20mm MEDIUM 1
C98007WZ1C20A-Plus DISC   WØ98   H25mm MEDIUM 1

Z COLOR  10 - INTENSIVE

     
C98002WZ1C10A-Plus DISC   WØ98   H14mm INTENSIVE 1
C98003WZ1C10A-Plus DISC   WØ98   H16mm INTENSIVE 1
C98004WZ1C10A-Plus DISC   WØ98   H18mm INTENSIVE 1
C98005WZ1C10A-Plus DISC   WØ98   H20mm INTENSIVE 1
C98007WZ1C10A-Plus DISC   WØ98   H25mm INTENSIVE 1

Z COLOR  01 - GREY LIGHT

     
C98003WZ1C01A-Plus DISC   WØ98   H16mm GREY LIGHT 1
C98006WZ1C01A-Plus DISC   WØ98   H22mm GREY LIGHT 1

ZYTTRIA® Z MULTICOLOR EXTRA-PLUS

APPLICATIONS

Zyttria ® Z MULTICOLOR EXTRA-PLUS is suitable for realizing individual crowns, bridges and circulars ( layered with ceramic or completely anatomic) .

 

DESCRIPTION

Polychromatic isostatic Zirconium Oxide with SIX LAYERS and HIGH PROGRESSIVE TRANSLUCENCY for an extraordinary "true to nature " effect.

The colours grade one into another from dentine to enamel with a exceptional progression of translucency that allows to simulate the natural tissue of the patient.

Available in four shades : Light / Medium / Intensive / Grey.

Sintering temperature:  1450°C/1500°C/1550°C

 

COLOURING

Colour liquids for brushing technique  AQUA-P.


 

 

 

Z MULTICOLOR  

     
C98004WML05A-Plus DISC   WØ98   H18mm LIGHT 1
C98004WML08A-Plus DISC   WØ98   H18mm MEDIUM 1
C98004WML10A-Plus DISC   WØ98   H18mm INTENSIVE 1
C98004WML01A-Plus DISC   WØ98   H18mm GREY  1
       
C98006WML05A-Plus DISC   WØ98   H22mm LIGHT 1
C98006WML08A-Plus DISC   WØ98   H22mm MEDIUM 1
C98006WML10A-Plus DISC   WØ98   H22mm INTENSIVE 1
C98006WML01A-Plus DISC   WØ98   H22mm GREY  1

RESIN & WAX

 PMMACAM

 

APPLICATIONS

Suitable for making provisional prosthesis, crowns and small bridges of 4/5 elements.

 

DESCRIPTION

100% Polymethilmethacrylate resin with excellent chemical stability and biocompatibility characteristics. Available in colours   A2, A3, B1. Other " Scala Vita" colours upon request.

 

Item Code Description Colour Pieces/Pack
C99PA9815W1-A2 MONOCOLOR DISC   Ø98mm   H15mm   A2 1
C99PA9815W1-A3 MONOCOLOR DISC   Ø98mm   H15mm   A3 1
C99PA9815W1-A35 MONOCOLOR DISC   Ø98mm   H15mm   A3.5 1
C99PA9815W1-B1 MONOCOLOR DISC   Ø98mm   H15mm   B1 1
C99PA9815W1-C2 MONOCOLOR DISC   Ø98mm   H15mm C2 1
C99PA9815W1-C3 MONOCOLOR DISC   Ø98mm   H15mm C3 1
C99PA9815W1-D2 MONOCOLOR DISC   Ø98mm   H15mm D2 1
C99PA9820W1-A2 MONOCOLOR DISC   Ø98mm   H20mm   A2 1
C99PA9820W1-A3 MONOCOLOR DISC   Ø98mm   H20mm   A3 1
C99PA9820W1-A35 MONOCOLOR DISC   Ø98mm   H20mm   A3.5 1
C99PA9820W1-B1 MONOCOLOR DISC   Ø98mm   H20mm   B1 1
C99PA9820W1-C2 MONOCOLOR DISC   Ø98mm   H20mm   C2 1
C99PA9820W1-C3 MONOCOLOR DISC   Ø98mm   H20mm   C3 1
C99PA9820W1-D2 MONOCOLOR DISC   Ø98mm   H20mm   D2 1
C99PA9820W1-PK MONOCOLOR DISC   Ø98mm   H20mm   PINK/Rosa 1

 

 

 POLYCAM

 

APPLICATIONS

Suitable for realizing crowns and long term provisional bridges.

 

DESCRIPTION

Resin. Available also in CLEAR version, suitable for making orthodontic bites.

 

 

 

Item Code Description Colour Pieces/Pack
C99PO9814W1-A2 MONOCOLOR DISC   Ø98mm   H14mm   A2 1
C99PO9814W1-A3 MONOCOLOR DISC   Ø98mm   H14mm   A3 1
C99PO9814W1-B1 MONOCOLOR DISC   Ø98mm   H14mm   B1 1
C99PO9814W1-C1 MONOCOLOR DISC   Ø98mm   H14mm   C1 1
C99PO9814W1-D2 MONOCOLOR DISC   Ø98mm   H14mm   D2 1
C99PO9818W1-A2 MONOCOLOR DISC   Ø98mm   H18mm   A2 1
C99PO9818W1-A3 MONOCOLOR DISC   Ø98mm   H18mm   A3 1
C99PO9818W1-B1 MONOCOLOR DISC   Ø98mm   H18mm   B1 1
C99PO9818W1-C1 MONOCOLOR DISC   Ø98mm   H18mm   C1 1
C99PO9818W1-D2 MONOCOLOR DISC   Ø98mm   H18mm   D2 1
       
C99PO9814W-CLEAR MONOCOLOR DISC   Ø98mm   H14mm   CLEAR 1

 

 MODELCAM

 

APPLICATIONS

Suitable for making models by cad-cam milling.

 

DESCRIPTION

Synthetic resin, easy to be milled and with high dimensional precision. Available in two different densities (0,95 - 1,60).

This is not a medical device.

 

 

Item Code Description   Pieces/Pack
C99M9825WLD DISC   WØ98mm   H25mm   LOW DENSITY(-) 1
C99M9828WHD DISC   WØ98mm   H28mm   HIGH DENSITY(+) 1

 

 PMMACAST

 

APPLICATIONS

Suitable for realizing structures through fusion technique and over pressing.

 

DESCRIPTION

Completely castable PMMA, useful to make structural tests of the oral cavity before performing the milling of Zirconia. 

This is not a medical device.

 

Item Code Description Colour Pieces/Pack
C99PC9816W1-AV DISC   Ø98mm   H16mm   YVORY/Avorio 1
C99PC9818W1-BL DISC   Ø98mm   H18mm   BLUE 1
C99PA9820W1-AV DISC   Ø98mm   H20mm   YVORY/Avorio 1

 

 CERAWAX

 

APPLICATIONS

Suitable for modeling structures made with the fusion technique.

 

DESCRIPTION

Castable wax.

This is not a medical device.

 

 

Item Code Description Colour Pieces/Pack
C99WX9815W1-B DISC   Ø98mm   H15mm   BLUE 1
C99WX9820W1-B DISC   Ø98mm   H20mm   BLUE 1
 
 
26 October 2016

ZYTTRIA® Z MULTICOLOR EXTRA-PLUS

Written by

 

ZYTTRIA® Z MULTICOLOR EXTRA-PLUS  1200-900Mpa

 

Progressive multilayer isostatic zirconia, particularly stable to create any prosthetic structure, even with complex geometries that require high technical performance.


 
Progressive translucency

Naturally progressive in the different chromatic layers, typical of the natural tissue of the tooth.

 

Progressive mechanical resistance

High mechanical strength from 1200 mpa in the marginal area to 900 mpa in the incisal area.


Applications    Single crowns, bridges (max 2 missing elements), circulars.

                            Ideal for complex restorations.
 
Colors                • A1  • A2  • A3 • B1  • C2   • D2                         
 
                            *Indicative values, approximated to the Vita® scale
 
                                Enamel area thickness > 3mm.
 

Characterization  In the green phase infiltration with colors AQUA-P 

 

Progression of chromatic intensity, mechanical resistance and translucency in the six layers

 

 

 



 

 
 

Applications    Single crowns, bridges (max 2 missing elements), circulars.

                            Ideal for complex restorations.
 
Colors                • A1  • A2  • A3 • B1  • C2   • D2                         
 
                            *Indicative values, approximated to the Vita® scale
 
                                Enamel area thickness > 3mm.
 

Characterization  In the green phase infiltration with colors AQUA-P 

 
 
 

 

 
 
 
 
Feb 2015
  • ISOSTATIC ZIRCONIA

  • HIGH TRANSLUCENCY

  • Sintering 1530°C - 1580°C   (see Sintering Cycle)

  


APPLICATION

It is used to realize single crowns, bridges and “full contour” elements.

Dental technicians appreciate Zirconia because it is easy to work with (CAD-CAM technology) and achieves an excellent aesthetic result. This characteristic feeds a growing interest in a more translucent material.

 


REMARKS ON  TRANSLUCENCY

Zirconia translucency depends on raw material and on sintering parameters. 

  •  Higher percentage of Aluminium Oxide in Zirconium Oxide powder means lower translucency

A poly-crystalline product is less translucent than a mono-crystalline one. Due to that Zirconia becomes more translucent by removing Alumina crystals.

 

  • Sintering parameters directly influence the level of Zirconia translucency

Micrographs carried out on Zirconia specimens with different sintering temperatures and permanence time at such temperatures, show that bigger crystals, resulting from higher sintering temperatures or longer permanence, give a greater translucency to the material.

At the same time, the grain size influences in a negative way the values of mechanical, hydrothermal  and aging resistance of Zirconia.

 

  • Raw material is essential to achieve translucency and to avoid the decline of technical characteristics

Hydrothermal and aging resistance, in particular, may have a severe decline if low quality raw materials are used. In this case it is possible to work Zirconia the same  respecting translucency requirements requested by dental technicians, but the final framework during the years may show problems due to the use of a unsuitable material.

ZYTTRIA® material produced by CONCEPT achieves a great result: Zyttria® Z402 EXTRA-TRASLUCENT has a very low content of Alumina (<0,1%) and a sintering temperature between 1500°C and 1530°C, crystals are big enough but with values that are not greater than 300nm.

All these characteristics guarantee a high translucency, but at the same time, suitable hydrothermal characteristics and restance to aging. 

 

The challenge continues: ZYTTRIA® Z402 EXTRA-TRASLUCENT PLUS 

Thanks to its technical know how CONCEPT has developed  ZYTTRIA® Z402 EXTRA-TRASLUCENT PLUS that unites high translucency and a very high level of technical performance which is a feature of Zirconia.


 

Feb 2015
  • ISOSTATIC ZIRCONIA
  • HOMOGENEOUS PRE-COLOURING
  • HIGH TRANSLUCENCY
  • HIGH MECHANICAL RESISTANCE
  • HIGH RESISTANCE TO AGING
  • Sintering at 1450°C – 1500°C – 1550°C (see Sintering Cycle)

 


High translucent pre-coloured Zirconia, available with different chromatic characteristics:

 

 

  • A1 pre-colored
  • A2 pre-colored
  • A3 pre-colored
  • B2 pre-colored
  • C2 pre-colored

 

 

The colouring of the prosthetic structure, after sintering, results homogeneous on the whole piece.

The ceramic pigments are mixed to the Zirconia powder with a technology that it is able to ensure to the granulate a uniform and constant colouring.

 

The pre-colored colors allow you to have the ideal base  to achieve the required tooth colour and they will avoid the dental laboratory to pay extra costs to create a stock. 

 

The final characterization of the prosthetic restoration is achieved by using dyes, glazes and through the ceramic layering.

 


 

 

 

Feb 2015
  •  ISOSTATIC ZIRCONIA
  • HIGH TRANSLUCENCY

  • AESTHETIC

  • HIGH MECHANICAL RESISTANCE

  • RESISTANCE TO AGING

  • Sintering at 1450°C – 1500°C – 1550°C  (see SINTERING CYCLE)

 


A new generation of white Zirconia with high translucency:

  • "True to nature" effect
  • Optical properties (transmission  and diffusion of light) similar to those of natural tooth tissue
  • High mechanical resistance (resistance to dynamic loading and aging)

 

APPLICATION

It is used to realize single crowns, bridges or “full contour” elements. In any case, it is possible to do ceramic layering.


  

Dental technicians, because of productivity and competitiveness, ask for very high milling and firing speed, together with the best aesthetic results, characteristics that are not always easy to optimize together.

Nevertheless, translucency is a a feature  that must be related to other characteristics, that are very important for healthcare when using Zirconia for the dental field.

The CONCEPT challenge is to create a material that fulfil the requirements of the modern orthodontics, considering  the responsibilities towards patients' health, with a product  that is able to guarantee very high technical and functional performances (flexural resistance, resistance to acid attacks and aging).

ZYTTRIA® Z402 EXTRA-TRASLUCENT PLUS was born for this purpose, a new generation Zirconia , very translucent at a low sintering temperature.

 

ATTENTION! 

The final aesthetic results of dental prostheses depend not only on material, but also on the processing.

In order to obtain the best translucency, it is essential that the processing is done with full respect of the material (see our User's Manual/Translucency).

 


 

Feb 2015

pmmacam 

 

  • 100% Polymethacrylate Resin

  • Excellent chemical stability and biocompatibility

  • Available in  A2, A3, B1 colors  

  • Other colors of “Vita Scale” upon request

 

APPLICATION

PMMA is suitable to create parts of dental provisional prostheses: crowns and small bridges of 4/5 elements. 


 

polycam

 

  • 100% Highly crosslinked polyamide resin

  • Biocompatible

  • High stability and resistance to shock

  • A2, A3, B1, CLEAR
     
     

APPLICATION

Suitable to create crowns and bridges for provisional long-term prostheses, substructures that may be united with Pmma products.

CLEAR version is excellent to create Orthodontic bites, suitable to treat Bruxism by avoiding dental wear due to the friction of the dental arches and by reducing the stress of tissues that support teeth.

PolyCam requires milling with water cooling.

 


pmmacast

 

  • Fully castable Pmma.

  • It burns without leaving residue.

  • Useful for structural tests in the oral cavity before the milling of Zirconia.

 

APPLICATION

Suitable to realize crowns and bridges by melting and overpressing.

Attention: This is not a medical device!

 

 


cerawax

 

  • Castable wax to model frameworks created with the fusion technique
  • It burns without leaving residue

Attention: This is not a medical device!

 


 

modelcam

 

  • Synthetic resin to create models by cad-cam milling

  • Excellent milling and dimensional precision

  •  Available in two different densities:

             - HIGH DENSITY (+) 

             - LOW DENSITY  (-)

Attention: This is not a medical device!